Process and joint quality of ultrasonic vibration enhanced friction stir lap welding

In order to improve the process effectiveness and joint quality, ultrasonic vibrations were integrated with friction stir lap welding. Effect of ultrasonic exertion on the process and joint quality of AA 6061-T6 were investigated. Upon ultrasonic exertion, joints owned larger effective lap width, shorter hooks and improved strength. Weld fracture mode changed from a ductile–brittle mixed mode to a more ductile mode while the fracture path shifted from lap interface to beyond the stir zone. Material flow and interface defects were characterised using lap welded dissimilar aluminium alloy joints. Ultrasonic vibration improved the material flow and reduced the interfacial defects. Variations in failure load of joints were found in accordance with the variations in material flow and interfacial defects.     

Investigation on the anti-reduction mechanism of Ti4+ in high dielectric constant system Ca0.9La0.067TiO3 by doping with Al2O3

Ca_0.9La_0.067TiO₃ (abbreviated as CLT) ceramics doped with different amount of Al₂O₃ were prepared via the solid state reaction method. The anti-reduction mechanism of Ti⁴⁺ in CLT ceramics was carefully investigated. X-ray diffraction (XRD) was used to analyze the phase composition and lattice structure. Meanwhile, the Rietveld method was taken to calculate the lattice parameters. X-ray photoelectron spectroscopy (XPS) was employed to study the valence variation of Ti ions in CLT ceramics without and with Al₂O₃. The results showed that Al³⁺ substituted for Ti⁴⁺ to form solid solution and the solid solubility limit of Al³⁺ is near 1.11 mol%. Furthermore, the reduction of Ti⁴⁺ in CLT ceramics was restrained by acceptor doping process and the Q × f values of CLT ceramics were improved significantly. The CLT ceramic doped with 1.11 mol% Al₂O₃ exhibited good microwave dielectric properties: ε_r = 141, Q × f = 6848 GHz, τ_f = 576 ppm/°C.     

Microstructure–mechanical property relationship in an Al–Mg alloy processed by constrained groove pressing-cross route

The constrained groove pressing-cross route process was implemented on a commercially annealed AA5052 alloy at room temperature, with up to two passes (strain of ～4.64) along the rolling direction and transverse direction. The results showed the formation of an ultrafine-grained structure with an average sub-grain/cell size in the 300–500?nm range. The indentation hardness and tensile strength increased significantly, up to ～75 and 105%, respectively, and became more homogenous with a uniform and isotropic trend, as compared to the annealed alloy. According to the Hall–Petch and Taylor models used, grain refinement and increasing dislocation density were proposed as the main strengthening mechanisms. Fractographic studies revealed a ductile-fracture behaviour, with a dimpled structure proportional to the UFG structure.     

The impact of the ICT4D project on sustainable rural development using a capability approach: Evidence from Bangladesh

Information and Communication Technology for Development (ICT4D) projects have shown a great promises in recent years. However, simply materializing of ICT4D projects is not enough for minimizing the prevalent digital divide in rural areas in developing countries. For the success of an Information and Communication Technology (ICT) intervention, it is important to consider the capabilities of users, who are responsible for converting ICT resources into outcome. While most of the ICT-related studies are focused on the adoption of actual technologies and influences of different internal and external factors on intervention outcomes, very few studies are focused on evaluating intervention outcomes and redesigning intervention strategies. In this study, I opted for using a conceptual framework following the Capability Approach that simultaneously identifies the influence factors for intervention outcome as well as evaluates the outcome based on Noble Laureate Amartya Sen’s five freedoms concept. A qualitative technique has been chosen to conduct the study. As part of the impact evaluation of an ICT4D intervention, a project known as Union Digital Centres (UDCs) in Bangladesh was selected. A total of ten themes are identified indicating that the outcome of the intervention is contributing to socio-economic and human development. However, the study has revealed that lack of capabilities of users (e.g. prior knowledge and financial inability) bar the UDC programs to fulfill their goals at highest level. This study would practically help the UDC policy makers to adjust the UDC intervention design by addressing the shortcomings of the users to yield higher UDC program outcome. Additionally, this study theoretically contributes in ICT adoption literature by showing that there is a mutual influence between users’ capabilities and ICT-related project outcomes. Finally, using specific case study (ICT4D project in Bangladesh), this study contextualizes Amartya Sen’s five freedoms concept in the ICT-specific context.     

An easy and scalable approach to synthesize three-dimensional sandwich-like Si/Polyaniline/Graphene nanoarchitecture anode for lithium ion batteries

A new three-dimensional (3D) sandwich-like Si/Polyaniline/Graphene nanoarchitecture anode for lithium ion batteries (LIBs) is successfully fabricated through an easy approach. In this nanoarchitecture, the in-situ polymerized electronic conductive polyaniline (PAni) hydrogel, acting as “glue”, agglutinates tightly to both the silicon nanoparticles (SiNPs) and graphene sheets, forming efficient conductive networks with high elastic modulus and high tensile strength. This mechanically robust nanoarchitecture can endure the great volume change of silicon and retain structural stability during Li-ion insertion/extraction. The electrodes consisting of this 3D sandwich-like Si/Polyaniline/Graphene nanoarchitecture reveal excellent electrochemical performance. The progress made in this work provides an easy and scalable route for preparing Si-based anode materials with high performance for advanced LIBs.     

焊丝中Si元素含量对铝合金接头裂纹敏感性的影响规律及机理

使用扫描电镜、能谱、温度场实时采集等测试方法，研究了焊丝中Si含量对AA6063铝合金GMAW焊接头热裂纹敏感性的影响规律及机理. 结果表明，当焊丝为纯铝时，鱼骨试样的焊缝中心会出现细长的焊接裂纹；当焊丝中的Si含量为4.5% ~ 6%时，裂纹的长度变短，但是开裂距离明显增加；当焊丝中的Si含量达到11% ~ 13%时，试样焊缝无裂纹出现. 随着Si含量的不断提高，合金易出现裂纹的凝固温度区间先增大后减小；焊丝中Si含量的不同还会影响凝固后期金属液的流动性，使得焊缝晶界处的物相成分和形态都有明显的区别；同时，Si含量的提高会使得接头的冷却速度先增加后减小，从而导致应力状态改变，热裂纹敏感性先升高后降低.     

时效工艺对纳米结构2297铝锂合金力学性能与微观组织的影响

采用535 ℃×2 h固溶制度,将热锻态2297铝锂合金固溶水淬后冷轧,冷轧压下量为95%,然后将轧制样品在不同温度(120~190 ℃)和时间(0~80 h)范围内进行时效处理。采用拉伸、扫描电镜(SEM)和透射电镜(TEM)等测试方法,分析时效温度和时间对铝锂合金组织与性能的影响。结果表明:时效前的大塑性变形能获得纳米结构组织,能促进T₁相均匀细小地析出,缩短合金达到峰时效的时间,最终成功制备了高强高塑性铝锂合金。在120~140 ℃温区内时效时,时效温度越高,达到峰时效的时间越短、强度越高。140 ℃达到峰时效时间缩短为40 h,此时合金的抗拉强度、屈服强度和伸长率分别为525 MPa、478 MPa和7.7%,主要强化相为细小的T₁相。在170~190 ℃温区内时效时,时效温度越高,达到峰时效的时间越短,但抗拉强度与屈服强度迅速下降。170 ℃时效8 h达到峰时效状态,此时合金的抗拉强度、屈服强度和伸长率分别是503 MPa、462 MPa和5.0%,主要强化相仍为T₁相,但已经明显粗化。     

Fe基非晶合金增强1060铝基多层复合材料的组织与性能

采用累积叠轧焊+中间退火法复合轧制1060Al/Fe基非晶多层铝合金复合板材。利用光学显微镜、扫描电镜、X-衍射分析仪以及拉伸试验机分析Al基复合材料的微观组织结构变化、断口形貌、物相组成以及力学性能。结果表明:Fe基非晶复合材料的增强体在300 ℃中间退火过程中发生部分晶化,在累积变形轧制过程中发生破碎,并随着变形道次的增加,破碎程度随之增大;复合板前6道次的累积轧制变形出现了明显的加工软化现象,并且随着变形道次的增加,其加工软化的效果愈明显;随着累积轧制变形道次增加,Al基复合材料的力学性能发生了明显的变化,第2道次轧制变形后屈服强度与抗拉强度达到了最大值为140 MPa和156 MPa,伸长率为5.53%,达到最佳综合性能。